Product Description
FIRE RETARDANT DOUBLE SIDED 8 LAYERS REFLECTIVE ALUMINIUM PAPER FOIL, 8x8 FIBERGLASS SCRIM REINFORCED
PRODUCT FEATURE
Customize size available upon request and machine capacity
TECHNICAL SPECIFICATION
Technical information provided in this data sheet are typical laboratory averages and are subject to variation.
While the information is believed to reliable and correct, no guarantee or warranty (expressed or implied) can be made regarding specific applications or patent right.
Product specifications are subject to change without prior notice
Product Description
FIRE RETARDANT DOUBLE SIDED 8 LAYERS REFLECTIVE ALUMINIUM PAPER FOIL, 8x8 FIBERGLASS SCRIM REINFORCED
PRODUCT FEATURE
- 99% Pure Aluminum Foil with high reflectivity (>0.98) and low emissivity (<0.02) surface.
- Reinforced with bidirectional (8x8) fiberglass scrim to increase the mechanical product strength and durability.
- Special bonding layers giving superior vapor barrier
- Comply with Fire Retardant properties in accordance to BS 476 Part 6 & 7
- Suggestion Size :
| Width(m) | Length (m) |
| 1.22 – 1.25 ± 2% | 60 ± 1% |
| Optimum packing pallet = 90 rolls | |
TECHNICAL SPECIFICATION
| GRAMMAGE | 210 – 230gsm |
| THICKNESS | 250 – 360 microns |
|
THERMAL RESISTANCE (ISO 8301,MS ISO8302) |
~1.375m2K/w |
|
REFLECTIVITY (ASTM C 1371) |
0.98 |
|
EMISSIVITY (ASTM C 1371) |
0.02 |
| RESISTANCE TO DRY LAMINATION (AS/NZS 4201.1) | No Delamination |
| RESISTANCE TO WET LAMINATION (AS/NZS 4201.1) | No Delamination |
|
VAPOUR BARRIER (ASTM E96) |
0.002 – 0.14μg/N.s |
|
SHRINKAGE (AS/NZS 4201.3) |
MD:<0.5% CD:<0.5% |
|
TENSILE STRENGTH (AS/NZS 1301.448s) |
MD:>5 kN/m CD:>3 kN/m |
|
EDGE TEAR RESISTANCE (TAPPI T470) |
MD:>30N CD:>20N |
|
FOLDING RESISTANCE (AS/NZS 1301.423rp) |
MD:>2.00 LOG10100 CD:>1.70 LOG10 50 |
| STUCTURE | FILM | 1 WAY | KRAFT | FILM |
| REINFORCEMENT |
Bidirectional Fiberglass Scrim (8x8 threads/100m) |
Technical information provided in this data sheet are typical laboratory averages and are subject to variation.
While the information is believed to reliable and correct, no guarantee or warranty (expressed or implied) can be made regarding specific applications or patent right.
Product specifications are subject to change without prior notice
 |
RECOMMENDED APPLICATION
|